YJS-601 carbon fiber impregnated plastic 
 Product Use: 
 Mainly used for the carbon fiber. Carbon fiber, the product has strong permeability, high tensile bond strength and splice strength; wear-resistant anti-corrosion, has high durability and excellent mechanical properties. 
 Technical indicators: 
 GB50367-2006 standard technical requirements. 
 Performance project to test the results of performance requirements (Class A) 
 Colloidal properties Tensile strength (Mpa) 41.6 ≥ 40 
 Tensile modulus of elasticity (Mpa) 2512 ≥ 2500 
 Elongation (%) 1.53 ≥ 1.5 
 Compressive Strength (Mpa) 73.4 ≥ 70 
 Bending strength (Mpa) 50.4 ≥ 50, and shall not be brittle (cataclastic) damage 
 Adhesion to steel - steel tensile shear strength of the standard value (Mpa) 14.9 ≥ 14 
 Steel - Steel uneven pull from the strength (Mpa) 20.3 ≥ 20 
 Concrete pull the bond strength (Mpa) 3.52, and the concrete cohesive failure ≥ 2.5, and cohesive failure of concrete 

 Use the methods and precautions: 
 1, YJS-601 carbon fiber impregnated with plastic Group A and Group B ratio of 3:1 mixture, mix well and use. 
 2, YJS-601 glue should be mixed in the 60 ~ 90min after use (depending on the ambient temperature may be). 
 3, the product density is about 1.15 ~ 1.25g/cm3 (cured), the gel time of about 3 to 6 hours. 
 Packing and storage: 
 Packaging specifications for the 18kg +6 kg / group 
 The product can be stored below 40 ℃ ambient temperature, the shelf life of 24 months. 
 3, the product is solvent, storage should be away from open flame heating device.